Fiberon™ PA12-CF10 1.75mm | 500g

£65.99

colour

Quantity

Item number: 6938936714637

Key Features:

High Performance filament PA12 reinforced with 10% carbon fibres
Low moisture
High strength
Warp-free™ technology

Application:

Aerospace
Automotive
Composite Manufacturing

Description

Polymaker Fiberon™ PA12-CF10 is carbon fiber reinforced long chain copolyimide filament. Thanks to its chemical structure, this product has lower moisture sensitivity compared to PA6/66 and PA6-based materials, and better mechanical properties than PA12-based materials. In addition, the carbon fiber reinforcement and Warp-free™ technology enhance the size stability of the prints produced with this material.

Specification

Diameter	1.75mm
Net weight	500grams

Recommendation

Temperature

Printing Temp:- 280 - 300˚C

Bed Temp:- 40 - 50°C

Printing Speed

Up to 300mm/s

Fan Speed

Closed Chamber

Not required

Surface

Adhesive

Drying

100˚C / 10h (Only if the material has absorbed moisture)

Nozzle

All-metal hotend above 280˚C and Hardened nozzle

Note

Abrasion of the brass nozzle happens frequently when printing Fiberon™ PA12-CF10. Normally, the life of a brass nozzle would be approximately 9h. A wear-resistance nozzle, such as hardened steel and ruby nozzle, is highly recommended to be used with Fiberon™ PA12-CF10.

Fiberon™ PA12-CF10 is sensitive to moisture and should always be stored and used under dry conditions (relative humidity below 20%).

If Fiberon™ PA12-CF10 is used as the support material for itself, please remove the support structure before excessive moisture absorption. Otherwise, the support structure can be permanently bonded to the model. After the printing process, it is recommended to anneal the model in the oven at 100°C for 16 hours.